Table 3. Representative analyses of Mg-rich and Fe-rich saponites.

Hole:
1024B
1025B
1026C
1026C
1026C
1026C
1027C
1027C
1027C
1027C
1027C
1027C
1027C
1027C
1028A
1028A
1028A
1028A
1029A
1029A
1031A
1031A
1031A
1032A
1032A
Core,section: 18X-CC 11X-CC 16R-1 17R-1 17R-1 17R-1 5R-5 4R-3 4R-3 4R-3 5R-5 5R-5 3R-2 3R-2 15X-7 15X-7 15X-7 15X-7 25X-4 25X-3 6X-1 6X-1 6X-1 12R-1 12R-1
Interval(cm): 10-37 34-40 40-45 13-17 13-17 13-17 22-27 85-91 85-91 85-91 22-27 22-27 115-117 115-117 15-18 15-18 15-18 15-18 7-12 77-82 49-52 49-52 49-52 126-132 126-132
Piece: 1 2 20 4 4 4 2 10 10 10 2 2 - - 2 2 2 2 2 11 10 10 10 19 19
Depth(mbsf): 167.83 97.53 238.90 238.63 238.63 238.63 628.95 617.49 617.49 617.49 628.95 628.95 606.25 606.25 132.89 132.89 132.89 132.89 221.14 220.57 41.79 41.79 41.79 291.46 291.46
Mineral Fe-rich Fe-rich Mg-rich Mg-rich Mg-rich Fe-rich Mg-rich Mg-rich Mg-rich Mg-rich Mg-rich Mg-rich Mg-rich Fe-rich Mg-rich Mg-rich Mg-rich Mg-rich Mg-rich Fe-rich Mg-rich Mg-rich Mg-rich Mg-rich Mg-rich
SiO2 49.83 48.01 47.87 47.34 48.52 49.88 52.52 50.36 50.48 51.23 49.30 50.16 49.34 47.60 50.56 48.25 47.81 50.52 49.58 48.37 45.80 49.03 48.64 49.44 49.58
TiO2 0.04 0.43 0.02 0.04 0.01 0.12 0.04 0.00 0.07 0.00 0.05 0.04 0.06 0.00 0.00 0.00 0.01 0.00 0.00 0.00 0.04 0.09 0.20 0.00 0.04
Al2O3 3.22 2.96 3.48 3.79 3.99 3.73 2.68 3.22 3.26 3.42 3.84 3.84 4.89 4.15 2.89 3.86 3.98 3.87 3.18 4.70 4.28 4.18 4.49 3.52 3.69
Cr2O3 0.08 0.06 0.06 0.00 0.00 0.00 0.22 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00
FeO 13.72 21.56 11.09 11.32 11.99 13.18 8.85 9.57 9.71 9.82 10.05 10.30 12.35 13.24 10.33 12.48 12.82 12.86 11.83 14.18 10.90 11.99 12.16 7.99 8.57
MgO 18.74 13.64 19.20 19.34 19.65 19.42 22.25 21.03 21.20 21.64 20.76 21.48 20.02 18.81 20.74 18.91 18.50 20.21 19.66 18.64 18.51 19.03 19.43 22.00 21.50
MnO 0.00 0.21 0.01 0.19 0.02 0.12 0.14 0.11 0.06 0.20 0.20 0.22 0.10 0.11 0.17 0.08 0.19 0.31 0.00 0.24 0.18 0.21 0.19 0.06 0.08
NiO 0.15 0.00 0.00 0.37 0.30 0.13 0.03 0.05 0.11 0.07 0.53 0.41 0.08 0.08 0.01 0.00 0.00 0.13 0.56 0.19 0.30 0.28 0.32 0.09 0.13
CaO 0.95 1.59 1.20 1.11 1.11 1.07 1.16 1.29 1.29 1.33 1.42 1.51 1.36 1.51 0.90 1.08 1.66 1.25 1.08 1.56 0.90 1.13 1.15 1.10 1.07
Na2O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.11 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00
K2O 0.40 0.27 0.09 0.22 0.08 0.11 0.27 0.12 0.13 0.13 0.22 0.14 0.22 0.11 0.43 0.51 0.00 0.51 0.57 0.16 0.44 0.31 0.39 0.32 0.26
Total 87.13 88.73 83.02 83.72 85.67 87.76 88.16 85.75 86.31 87.84 86.37 88.10 88.42 85.72 86.03 85.17 84.97 89.66 86.46 88.04 81.35 86.25 86.97 84.52 84.92
Si 7.493 7.418 7.457 7.359 7.366 7.418 7.591 7.519 7.496 7.479 7.375 7.356 7.269 7.293 7.558 7.397 7.360 7.371 7.474 7.248 7.324 7.399 7.302 7.446 7.448
Al(IV) 0.507 0.539 0.543 0.641 0.634 0.582 0.409 0.481 0.504 0.521 0.625 0.644 0.731 0.707 0.442 0.603 0.640 0.629 0.526 0.752 0.676 0.601 0.698 0.554 0.552
Ti 0.005 0.050 0.002 0.005 0.001 0.013 0.004 0.000 0.008 0.000 0.006 0.004 0.007 0.000 0.000 0.000 0.001 0.000 0.000 0.000 0.005 0.010 0.023 0.000 0.005
Al(VI) 0.064 0.000 0.095 0.054 0.079 0.072 0.047 0.085 0.067 0.067 0.052 0.019 0.118 0.042 0.067 0.095 0.082 0.036 0.038 0.078 0.131 0.142 0.096 0.070 0.102
Fet 1.725 2.786 1.445 1.472 1.522 1.639 1.070 1.195 1.206 1.199 1.257 1.263 1.522 1.696 1.291 1.600 1.651 1.569 1.491 1.777 1.458 1.513 1.527 1.006 1.077
Cr 0.010 0.007 0.007 0.000 0.000 0.000 0.025 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000
Mg(VI) 4.179 3.129 4.449 4.399 4.358 4.245 4.793 4.680 4.692 4.701 4.596 4.637 4.332 4.238 4.619 4.295 4.241 4.341 4.402 4.092 4.344 4.274 4.292 4.905 4.791
Mn 0.000 0.027 0.001 0.025 0.003 0.015 0.017 0.014 0.008 0.025 0.025 0.027 0.012 0.014 0.022 0.010 0.025 0.038 0.000 0.030 0.024 0.027 0.024 0.008 0.010
Ni 0.018 0.000 0.000 0.046 0.037 0.016 0.003 0.006 0.013 0.008 0.064 0.048 0.009 0.010 0.001 0.000 0.000 0.015 0.068 0.023 0.039 0.034 0.039 0.011 0.016
Mg 0.021 0.012 0.009 0.082 0.088 0.060 0.000 0.000 0.000 0.007 0.033 0.058 0.064 0.058 0.002 0.027 0.004 0.054 0.015 0.071 0.069 0.007 0.056 0.034 0.023
Ca 0.153 0.263 0.200 0.185 0.181 0.170 0.180 0.206 0.205 0.208 0.228 0.237 0.215 0.248 0.144 0.177 0.274 0.195 0.174 0.250 0.154 0.183 0.185 0.177 0.172
Na 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.033 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000 0.000
K 0.077 0.053 0.018 0.044 0.015 0.021 0.050 0.023 0.025 0.024 0.042 0.026 0.041 0.021 0.082 0.100 0.000 0.095 0.110 0.031 0.090 0.060 0.075 0.061 0.050

Notes: Formulas have been calculated on the basis of 20 oxygens and four hydroxyls per unit cell, considering (Si + Al)IV = 8 a.p.f.u. and assigning the remaining Al to the octahedral sites together with Fe and Mg. The Mg excess in octahedral sites has been assigned to the interlayer positions.