Table
T12. Total sulfur and water concentration in samples
analyzed by ICP-AES and unignited XRD samples, Hole 1188A.
Core,
section,
interval (cm)Curated
depth
(mbsf)Total
Sulfur (wt%)
H2O+
unignited
(wt%)
193-1188A-
2R-1,
9-12
9.69
0.02
ND
ND
1.21
5R-1,
38-40
33.98
0.06
ND
ND
ND
5R-1,
42-45
44.04
0.65
ND
0.02
7.93
7R-1,
62-64
48.82
4.66
0.74
0.36
4.75
7R-1,
92-93
49.12
2.81
ND
ND
ND
7R-1,
119-120
49.39
2.56
ND
ND
ND
7R-1,
145-147
49.65
9.24
ND
ND
ND
7R-2,
39-41
50.09
3.78
0.73
0.20
5.09
7R-2,
51-53
50.21
6.80
ND
ND
ND
8R-1,
66-69
58.56
2.53
0.32
0.15
5.42
8R-1,
124-127
59.14
5.00
0.63
0.20
4.90
8R-1,
147-148
59.37
7.44
ND
ND
ND
9R-1,
13-14
67.73
0.58
ND
ND
ND
9R-1,
67-70
68.27
4.33
0.21
0.09
3.63
9R-2,
79-81
69.89
5.13
ND
0.20
3.34
10R-1,
35-37
77.65
0.93
ND
ND
ND
11R-1,
35-38
87.25
5.47
0.53
0.33
3.49
11R-1,
56-57
87.46
4.75
ND
ND
ND
12R-1,
51-52
97.11
2.68
ND
ND
ND
12R-1,
69-70
97.29
2.88
ND
ND
ND
12R-1,
117-118
97.77
0.33
ND
ND
ND
12R-2,
48-51
98.56
0.63
0.01
ND
1.54
13R-1,
9-12
106.39
1.37
ND
ND
ND
14R-1,
44-45
116.47
3.95
0.69
0.06
3.08
14R-1,
92-93
116.92
1.73
ND
ND
ND
14R-1,
105-108
117.05
2.98
1.09
0.06
2.53
16R-1,
77-78
136.17
3.09
ND
ND
ND
16R-1,
95-98
136.35
3.42
0.56
0.03
3.24
16R-2,
12-15
136.98
3.63
ND
ND
0.87
16R-2,
40-43
137.26
2.16
0.11
BD
0.68
16R-2,
51-52
137.37
2.38
ND
ND
ND
16R-2,
68-69
137.54
2.41
ND
ND
ND
17R-1,
90-93
146.00
0.99
0.01
0.04
3.36
17R-1,
123-124
146.33
4.02
ND
ND
ND
18R-1,
28-29
154.98
1.12
ND
ND
ND
19R-1,
73-76
165.03
0.49
BD
ND
1.44
20R-1,
46-47
174.36
3.99
ND
ND
ND
20R-1,
74-77
174.62
5.98
BD
ND
2.33
20R-1,
75-76
174.64
5.98
BD
ND
2.33
20R-1,
92-95
174.82
2.79
BD
ND
2.17
20R-1,
102-103
174.92
4.23
ND
ND
ND
21R-1,
20-21
183.30
0.39
BD
ND
2.18
Notes: ICP-AES = inductively coupled plasma-atomic emission spectroscopy, XRD = X-ray diffraction. * = ignited at 600°C for 6 hr and then at 1050°C for 1 hr, † = ignited at 600°C for 6 hr and then at 1050°C for 4 hr. Detection limit = 0.01%. Instrument precision = ±0.04%. ND = not determined, BD = below detection. Loss on ignition (LOI) on Hole 1188A samples was carried out at 1050°C for 1 hr. Additionally, total sulfur post-LOI for the ICP-AES samples are reported.