Leg
|
Site
|
Hole
|
Core
|
Type
|
Section
|
Top
(cm)
|
Depth
(mbsf) |
Magnetic
susceptibility
(10–5 SI)
|
NRM_Int
(A/m)
|
MDF
(mT) |
Q
|
---|---|---|---|---|---|---|---|---|---|---|---|
210 | 1277 | A | 1 | W | 1 | 108 | 1.08 | 256 | 1.35 | 8 | 13.32 |
210 | 1277 | A | 1 | W | 2 | 24 | 1.6 | 565 | 3.62 | 5 | 16.18 |
210 | 1277 | A | 1 | W | 2 | 100 | 2.36 | 347 | 0.428 | 7.5 | 3.12 |
210 | 1277 | A | 2 | R | 1 | 28 | 104.18 | 20 | 0.691 | 15 | 87.27 |
210 | 1277 | A | 2 | R | 1 | 114 | 105.04 | 10 | 0.215 | 15 | 54.31 |
210 | 1277 | A | 5 | R | 2 | 8 | 134.11 | 2346 | 0.156 | 28 | 0.17 |
210 | 1277 | A | 5 | R | 2 | 12 | 134.15 | 644 | 0.155 | 20 | 0.61 |
210 | 1277 | A | 5 | R | 2 | 24 | 134.27 | 689 | 0.238 | 28.5 | 0.87 |
210 | 1277 | A | 5 | R | 2 | 26 | 134.29 | 379 | 0.374 | 28 | 2.49 |
210 | 1277 | A | 5 | R | 2 | 30 | 134.33 | 761 | 0.698 | 25 | 2.32 |
210 | 1277 | A | 5 | R | 2 | 66 | 134.69 | 598 | 1.07 | 22 | 4.52 |
210 | 1277 | A | 7 | R | 1 | 56 | 152.36 | 475 | 2.25 | 12 | 11.96 |
210 | 1277 | A | 7 | R | 1 | 64 | 152.44 | 1490 | 1.33 | 10 | 2.25 |
210 | 1277 | A | 7 | R | 1 | 82 | 152.62 | 548 | 1.23 | 14 | 5.67 |
210 | 1277 | A | 7 | R | 1 | 110 | 152.9 | 1539 | 1.34 | 10 | 2.20 |
210 | 1277 | A | 7 | R | 2 | 46 | 153.69 | 1379 | 0.855 | 7 | 1.57 |
210 | 1277 | A | 7 | R | 2 | 58 | 153.81 | 87 | 0.152 | 15 | 4.41 |
210 | 1277 | A | 7 | R | 2 | 74 | 153.97 | 247 | 0.41 | 19 | 4.19 |
210 | 1277 | A | 7 | R | 2 | 90 | 154.13 | 187 | 0.208 | 6 | 2.81 |
210 | 1277 | A | 7 | R | 2 | 118 | 154.41 | 139 | 0.232 | 25 | 4.22 |
210 | 1277 | A | 8 | R | 1 | 78 | 162.28 | 52 | 0.089 | 21 | 4.32 |
210 | 1277 | A | 8 | R | 1 | 112 | 162.62 | 2016 | 1.39 | 15 | 1.74 |
210 | 1277 | A | 8 | R | 1 | 124 | 162.74 | 1205 | 1.56 | 19.5 | 3.27 |
210 | 1277 | A | 8 | R | 1 | 142 | 162.92 | 48 | 0.023 | 49 | 1.21 |
210 | 1277 | A | 8 | R | 2 | 24 | 163.19 | 1962 | 1.49 | 8 | 1.92 |
210 | 1277 | A | 8 | R | 2 | 42 | 163.37 | 851 | 0.832 | 12 | 2.47 |
210 | 1277 | A | 8 | R | 2 | 46 | 163.41 | 666 | 0.513 | 20 | 1.95 |
210 | 1277 | A | 8 | R | 2 | 48 | 163.43 | 612 | 0.349 | 20 | 1.44 |
210 | 1277 | A | 9 | R | 3 | 30 | 173.97 | 1575 | 4.03 | 4 | 6.46 |
210 | 1277 | A | 9 | R | 3 | 64 | 174.31 | 749 | 1.55 | 7 | 5.23 |
210 | 1277 | A | 9 | R | 3 | 70 | 174.37 | 636 | 1.21 | 12 | 4.81 |
210 | 1277 | A | 9 | R | 3 | 76 | 174.43 | 605 | 2.88 | 9.8 | 12.02 |
210 | 1277 | A | 9 | R | 3 | 120 | 174.87 | 2618 | 4.69 | 5 | 4.52 |
210 | 1277 | A | 9 | R | 4 | 18 | 175.19 | 1617 | 5.42 | 4.5 | 8.47 |
210 | 1277 | A | 9 | R | 4 | 50 | 175.51 | 1140 | 2.54 | 9.7 | 5.63 |
210 | 1277 | A | 9 | R | 4 | 62 | 175.63 | 660 | 1.9 | 9.8 | 7.27 |
210 | 1277 | A | 9 | R | 4 | 120 | 176.21 | 1354 | 3.65 | 7 | 6.81 |
210 | 1277 | A | 9 | R | 5 | 58 | 177 | 1232 | 1.4 | 9.8 | 2.87 |
210 | 1277 | A | 9 | R | 5 | 66 | 177.08 | 952 | 0.436 | 10 | 1.16 |
210 | 1277 | A | 9 | R | 5 | 86 | 177.28 | 1305 | 0.505 | 16 | 0.98 |
210 | 1277 | A | 9 | R | 5 | 92 | 177.34 | 1266 | 1.21 | 7.5 | 2.41 |
210 | 1277 | A | 9 | R | 6 | 10 | 177.82 | 2661 | 3.19 | 4 | 3.03 |
210 | 1277 | A | 9 | R | 6 | 44 | 178.16 | 1543 | 1.93 | 5 | 3.16 |
210 | 1277 | A | 9 | R | 6 | 124 | 178.96 | 1811 | 2.96 | 5 | 4.13 |
210 | 1277 | A | 9 | R | 7 | 8 | 179.16 | 732 | 1.61 | 6.8 | 5.56 |
210 | 1277 | A | 9 | R | 7 | 38 | 179.46 | 571 | 1.63 | 4.9 | 7.21 |
210 | 1277 | A | 9 | R | 7 | 66 | 179.74 | 1343 | 2.04 | 4.7 | 3.84 |
210 | 1277 | A | 9 | R | 7 | 88 | 179.96 | 1471 | 2.7 | 5 | 4.64 |
210 | 1277 | A | 9 | R | 7 | 122 | 180.3 | 1933 | 3.02 | 4.6 | 3.95 |
210 | 1277 | A | 9 | R | 8 | 14 | 180.51 | 1410 | 2.92 | 5 | 5.23 |
210 | 1277 | A | 9 | R | 8 | 24 | 180.61 | 1301 | 1.49 | 5 | 2.89 |
210 | 1277 | A | 9 | R | 8 | 40 | 180.77 | 1345 | 1.88 | 3.5 | 3.53 |
Notes: NRM_Int = remanent magnetization intensity, MDF = median destructive field, Q = Königsberger ratio. W = wash core, R = rotary core barrel.