Core, section,
interval (cm) |
Depth
(mbsf) |
Sample
number |
Major element oxides (wt%)
|
|||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
SiO2
|
Al2O3
|
Fe2O3
|
MgO
|
CaO
|
Na2O
|
K2O
|
TiO2
|
MnO
|
P2O5
|
LOI
|
Total
|
|||
| 210-1277A- | ||||||||||||||
| 1W-1,36–39 | 0.93 | AR123A | 39.89 | 16.59 | 5.6 | 3.11 | 18.98 | 2.97 | 0.368 | 1.092 | 0.23 | 0.124 | 10.31 | 99.26 |
| 1W-1,36–39 | 0.93 | AR123B | 40.97 | 16.91 | 5.88 | 3.24 | 18.68 | 3.06 | 0.397 | 1.122 | 0.228 | 0.131 | 9.69 | 100.31 |
| 1W-2, 62–66 | 1.98 | AR124 | 43.15 | 16.41 | 7.71 | 4.31 | 15.82 | 3.22 | 0.471 | 1.124 | 0.239 | 0.145 | 7.49 | 100.09 |
| 3R-1, 84–87 | 114.40 | AR126 | 44.24 | 14.56 | 10.3 | 4.4 | 13.73 | 2.67 | 2.015 | 1.411 | 0.135 | 0.186 | 6.79 | 100.24 |
| 3R-3, 46–49 | 116.97 | AR130 | 35.77 | 11.16 | 8.15 | 5 | 20.42 | 2.15 | 1.919 | 1.126 | 0.124 | 0.196 | 14.37 | 100.29 |
| 3R-1, 84–87 | 114.40 | AR126 | 44.24 | 14.56 | 10.3 | 4.4 | 13.73 | 2.67 | 2.015 | 1.411 | 0.135 | 0.186 | 6.79 | 100.24 |
| 3R-3,131–135 | 117.82 | AR125 | 48.68 | 15.89 | 9.08 | 5.93 | 9.92 | 2.97 | 1.856 | 1.581 | 0.124 | 0.207 | 3.59 | 99.83 |
| 3R-4, 61–65 | 118.57 | AR129 | 21.55 | 5.47 | 5.63 | 6.51 | 32.12 | 0.86 | 1.123 | 0.507 | 0.152 | 0.099 | 26.37 | 100.29 |
| 4R-3, 2–6 | 125.96 | AR127 | 48.66 | 15.22 | 8.35 | 8 | 7.49 | 2.77 | 1.865 | 1.273 | 0.097 | 0.147 | 3.45 | 99.01 |
| 5R-1, 52–55 | 133.12 | AR128 | 49.12 | 15.79 | 9.34 | 6.34 | 9.64 | 3.12 | 2.091 | 1.334 | 0.113 | 0.157 | 3.43 | 100.38 |
Notes: LOI = loss on ignition. X-ray fluorescence analyses performed at the Institute of Earth Science, University of Edinburgh (United Kingdom), using the method specified by Fitton et al. (1998).
Table T1 (continued).
|
Core, section,
interval (cm)
|
Depth
(mbsf)
|
Sample
number
|
Trace elements (ppm)
|
||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
Nb
|
Zr
|
Y
|
Sr
|
Rb
|
La
|
Ce
|
Nd
|
Zn
|
Cu
|
Ni
|
Cr
|
V
|
Ba
|
Sc
|
|||
| 210-1277A- | |||||||||||||||||
| 1W-1,36–39 | 0.93 | AR123A | 2.1 | 76.2 | 27.9 | 157.1 | 4.7 | 3.6 | 14.9 | 11.6 | 92.1 | 84.4 | 134.1 | 403.7 | 317.3 | 51.5 | 50.4 |
| 1W-1,36–39 | 0.93 | AR123B | 2.1 | 77.6 | 28.1 | 148.6 | 5.2 | 5.0 | 14.3 | 10.1 | 90.6 | 83.7 | 146.0 | 411.9 | 325.8 | 55.2 | 48.8 |
| 1W-2, 62–66 | 1.98 | AR124 | 1.9 | 77.7 | 31.6 | 146.9 | 5.5 | 5.2 | 13.6 | 9.6 | 76.8 | 76.1 | 145.7 | 381.2 | 308.4 | 31.7 | 48.3 |
| 3R-1, 84–87 | 114.40 | AR126 | 4.4 | 117.9 | 33.1 | 141.5 | 24.4 | 6.1 | 18.0 | 15.1 | 117.0 | 51.8 | 121.8 | 191.7 | 275.2 | 79.4 | 39.4 |
| 3R-3, 46–49 | 116.97 | AR130 | 3.1 | 91.9 | 27.7 | 127.3 | 25.7 | 6.4 | 19.7 | 14.6 | 117.1 | 26.9 | 157.9 | 239.9 | 263.3 | 44.4 | 34.4 |
| 3R-1, 84–87 | 114.40 | AR126 | 4.4 | 117.9 | 33.1 | 141.5 | 24.4 | 6.1 | 18.0 | 15.1 | 117.0 | 51.8 | 121.8 | 191.7 | 275.2 | 79.4 | 39.4 |
| 3R-3,131–135 | 117.82 | AR125 | 5.0 | 129.8 | 36.2 | 153.7 | 19.3 | 5.7 | 22.3 | 17.5 | 116.7 | 33.7 | 133.2 | 155.1 | 263.0 | 50.8 | 37.7 |
| 3R-4, 61–65 | 118.57 | AR129 | 1.2 | 46.3 | 16.1 | 87.7 | 15.2 | 6.3 | 11.4 | 10.0 | 71.3 | 28.0 | 451.3 | 810.0 | 150.6 | 17.0 | 25.0 |
| 4R-3, 2–6 | 125.96 | AR127 | 4.0 | 108.2 | 27.5 | 127.5 | 27.5 | 4.9 | 16.8 | 12.6 | 85.4 | 54.4 | 290.3 | 209.2 | 228.5 | 57.6 | 31.5 |
| 5R-1, 52–55 | 133.12 | AR128 | 3.7 | 106.1 | 29.3 | 145.9 | 36.9 | 5.3 | 17.2 | 12.2 | 76.6 | 40.5 | 152.2 | 232.0 | 249.4 | 55.6 | 34.1 |